Axial Compression Performance of Slender Concrete-Filled Circular Steel Tubular Column with Pitting Corrosion Damage

Jianwei Li; Lanlan Wang; Chen Jia; Lanhui Guo

doi:10.13206/j.gjgS23111502

Volume 39 Issue 7

Jul. 2024

Turn off MathJax

Article Contents

Article Navigation > STEEL CONSTRUCTION(Chinese & English) > 2024 > 39(7): 47-54

Jianwei Li, Lanlan Wang, Chen Jia, Lanhui Guo. Axial Compression Performance of Slender Concrete-Filled Circular Steel Tubular Column with Pitting Corrosion Damage[J]. STEEL CONSTRUCTION(Chinese & English), 2024, 39(7): 47-54. doi: 10.13206/j.gjgS23111502

Citation:

Jianwei Li, Lanlan Wang, Chen Jia, Lanhui Guo. Axial Compression Performance of Slender Concrete-Filled Circular Steel Tubular Column with Pitting Corrosion Damage[J]. STEEL CONSTRUCTION(Chinese & English), 2024, 39(7): 47-54. doi: 10.13206/j.gjgS23111502

Citation:

PDF( 8424 KB)

Axial Compression Performance of Slender Concrete-Filled Circular Steel Tubular Column with Pitting Corrosion Damage

doi: 10.13206/j.gjgS23111502

1. School of Civil Engineering, Harbin Insitute of Technology, Harbin 150090, China;
2. Jilin Research and Design Institute of Building Science, Changchun 130011, China

Received Date: 2023-11-15
Available Online: 2024-08-16

Abstract

Abstract

Localized pitting corrosion damage can cause an adverse impact on the safety of concrete-filled steel tubes (CFST). This paper conducted a numerical analysis of the axial compression performance of slender CFST with pitting corrosion damage. The failure phenomenon and load-deformation relationships from the existing tests were used to verify the numerical models. Then, the verified models were extended to take the random characteristics of corrosion pits in the aspect of distribution, dimensions, and locations into account. The influence of the degree of local volume loss, material strength, and slenderness ratio on the load-deflection curves was analyzed. According to the same degree of local volume loss, the CFST with equivalent thickness loss was established. The different influences of pitting corrosion and equivalent local defect on the ultimate strength were compared. Finally, based on the equivalent thickness loss, three methods based on the Chinese codes were put forward and to calculate the axial compression performance of CFST column with pitting corrosion damage and compare with the result of FE analysis.
The results show that the influence caused by different distributions of corrosion depth could be ignored. Compared with the equivalent local defect, the pitting corrosion can have a greater decrease in the ultimate strength of the slender CFST. According to the degree of local volume loss, the methods based on GB 50936- 2014 could predict the ultimate strength of CFST with pitting corrosion damage, and the method based on GB 50936-2014 could provide a prediction with good accuracy and moderate consideration.
- concrete-filled circular steel tubular,
- random pitting corrosion,
- axial compression performance,
- finite element analysis

FullText(HTML)

References(25)

References

[1]	Han L H, Hou C C, Wang Q L. Behavior of circular CFST stub columns under sustained load and chloride corrosion[J]. Journal of Constructional Steel Research, 2014,103(12):23-36.
[2]	Hou C C, Han L H, Wang Q L, et al. Flexural behavior of circular concrete filled steel tubes (CFST) under sustained load and chloride corrosion[J]. Thin-Walled Structures, 2016, 107:182-196.
[3]	贾晨,邵永松,郭兰慧,等.建筑结构用钢的大气腐蚀模型研究综述[J].哈尔滨工业大学学报, 2020,52(8):1-9.
[4]	Guo L, Huang H, Jia C, et al. Axial behavior of square CFST with local corrosion simulated by artificial notch[J]. Journal of Constructional Steel Research, 2020,174,106314.
[5]	Yuan F, Chen M, Huang H, et al. Circular concrete filled steel tubular (CFST) columns under cyclic load and acid rain attack:test simulation[J]. Thin-Walled Structures, 2018, 122(1):90-101.
[6]	Xie L, Chen M C, Sun W, et al. Behaviour of concrete-filled steel tubular members under pure bending and acid rain attack:test simulation[J]. Advances in Structural Engineering, 2019,22(1):240-253.
[7]	Han L H, Hua Y X, Hou C, et al. Circular concrete-filled steel tubes subjected to coupled tension and chloride corrosion[J]. Journal of Structural Engineering, 2017,143(10),04017134.
[8]	Hua Y X, Han L H, Wang Q L, et al. Behaviour of square CFST beam-columns under combined sustained load and corrosion:experiments[J]. Thin-Walled Structures, 2019,136:353-366.
[9]	Guo L H, Li J W, Jia C, et al. Axial compression behavior of slender concrete-filled steel tubes with machining defects representing local corrosion[J]. Engineering Structures, 2023, 286,116091.
[10]	Huang H, Guo L, Qu B, et al. Tests of circular concrete-filled steel tubular stub columns with artificial notches representing local corrosions[J]. Engineering Structures, 2021,242(8),112598.
[11]	Zhong L, Guo L, Jia C. Axial compression behavior of stub square concrete-filled steel tubes with regional defect[J]. Engineering Structures, 2023,278,115510.
[12]	Lin S Q, Li Z L, Zhao Y G. Behavior of eccentrically loaded circular concrete-filled steel tube stub columns with localized corrosion[J]. Engineering Structures, 2023,288,116227.
[13]	李振林,林思奇,赵衍刚,等.局部腐蚀钢管混凝土短柱轴压性能试验研究[J].工程力学, 2023,40(8):170-180.
[14]	Luo S, Chen M, Huang H, et al. Eccentric compression test and ultimate load strength analysis of circular CFST long column with local corrosion[J]. Structures, 2023,56,104937.
[15]	Li G, Hou C, Shen L. Combined compression-bending performance and design of CFST with localised pitting corrosion[J]. Journal of Constructional Steel Research, 2022,192,107247.
[16]	Tao Z, Wang Z, Yu Q. Finite element modelling of concrete-filled steel stub columns under axial compression[J]. Journal of Constructional Steel Research, 2013,89:121-131.
[17]	王文静,耿焘,贾晓楠,等.腐蚀对结构受力的影响以及改进措施[J].中国工程机械学报, 2014(2):118-122.
[18]	Nakai T, Matsushita H, Yamamoto N. Effect of pitting corrosion on strength of web plates subjected to patch loading[J]. ThinWalled Structures, 2006,44(1):10-19.
[19]	Rivas D, Caleyo F, Valor A, et al. Extreme value analysis applied to pitting corrosion experiments in low carbon steel:comparison of block maxima and peak over threshold approaches[J]. Corrosion Science, 2008,50(11):3193-3204.
[20]	张威.锈蚀钢筋表面特征的统计分析及其力学性能退化模型研究[D].西安:西安建筑科技大学, 2013.
[21]	Nakai T, Matsushita H, Yamamoto N, et al. Effect of pitting corrosion on local strength of hold frames of bulk carriers (1st report)[J]. Marine Structures, 2004,17(5):403-432.
[22]	Nakai T, Matsushita H, Yamamoto N. Effect of pitting corrosion on local strength of hold frames of bulk carriers (2nd report):lateral-distortional buckling and local face buckling[J]. Marine Structures, 2004,17(8):612-641.
[23]	中华人民共和国住房和城乡建设部.钢管混凝土结构技术规范:GB 50936-2014[S].北京:中国建筑工业出版社,2014.
[24]	中国工程建设标准化协会.钢管混凝土结构技术规程:CECS 28:2012[S].北京:中国计划出版社,2012.
[25]	福建省住房和城乡建设厅.钢管混凝土结构技术规程:DBJ/T 13-51-2010[S].福州:福建省住房和城乡建设厅,2010.